Schematic of the angle between the magnetic field axis and ribbon axis The annealing treatment was accomplished at 250°C
Source publication
Solid-State and Integrated Circuit Technology (ICSICT), 2014 12th IEEE International Conference on
Cobalt-based amorphous ribbons (Metglas® 2714A) were annealed treatment with an applied magnetic field. During annealing, the angle between the magnetic field axis and ribbon axis was designed for 0°, 30°, 60° and 90° respectively. MEMS technology was...
Contexts in source publication
Context 1
... the measurement of GMI ratio of the ribbon with different annealing orientation treatment was performed. The field dependence of the GMI ratio for 978-1-4799-3282-5/14/$3l.00 m014 IEEE micro-patterned Co-based ribbons is shown in Fig.3.A. ...
Similar publications
In this paper, micro-patterned cobalt-based amorphous ribbons with different structures are fabricated by MEMS technology, including bonding, lithography and electroplating. The commercial amorphous ribbons (VITROVAC 6025Z) are purchased from VACUUMSHMELZE® company. The structures of micro-patterned ribbons are designed for meander shape for differ...
Enhanced giant magnetoimpedance (GMI) effect has been observed in micro-patterned Co-based Metglas 2705M amorphous magnetic ribbons coated with single-layer graphene. The micro-patterned ribbon was designed for tortuous structure and fabricated by MEMS technology, and the graphene thin film was developed by spin coating and dispensing method onto t...