Article

The use of Apatite II (TM) to remove divalent metal ions zinc(II), lead(II), manganese(II) and iron(II) from water in passive treatment systems: Column experiments

Department of Mining Engineering and Natural Resources, Universitat Politècnica de Catalunya, Bases de Manresa 61-73, 08242 Manresa, Catalonia, Spain.
Journal of hazardous materials (Impact Factor: 4.53). 12/2010; 184(1-3):364-74. DOI: 10.1016/j.jhazmat.2010.08.045
Source: PubMed

ABSTRACT

The conventional passive treatments for remediation of acid mine drainage using calcite are not totally efficient in the removal of certain heavy metal ions. Although pH increases to 6-7 and promotes the precipitation of trivalent and some divalent metals as hydroxides and carbonates, the remaining concentrations of some divalent metals ions do not fulfill the environmental regulations. In this study, Apatite II™, a biogenic hydroxyapatite, is used as an alternative reactive material to remove Zn(II), Pb(II), Mn(II) and Fe(II). Apatite II™ reacted with acid water releasing phosphate and increasing pH up to 6.5-7, inducing metals to precipitate mainly as metal-phosphates: zinc precipitated as hopeite, Zn(3)(PO(4))(2)·4H(2)O, lead as pyromorfite, Pb(5)(PO(4))(3)OH, manganese as metaswitzerite, Mn(3)(PO(4))(2)·4H(2)O and iron as vivianite, Fe(3)(PO(4))(2)·8H(2)O. Thus, metal concentrations from 30 to 75 mg L(-1) in the inflowing water were depleted to values below 0.10 mg L(-1). Apatite II™ dissolution is sufficiently fast to treat flows as high as 50 m/a. For reactive grain size of 0.5-3mm, the treatment system ends due to coating of the grains by precipitates, especially when iron and manganese are present in the solution.

Download full-text

Full-text

Available from: Jose Luis Cortina
  • Source
    • "Due to the influences of coexisting cations and the presence of dissolved Fe 3+ in natural waters at low levels [12], separation and preconcentration before determination are usually necessary. Many absorbents have been reported for removal of iron ions (Fe 2+ or Fe 3+ ) [13] [14] [15] [16]. Therefore, our study is focused on this area. "
    [Show abstract] [Hide abstract]
    ABSTRACT: Abstract Pentane-1,2-dicarboxylic acid functionalized spherical MCM-41 nanoparticles (DA-MCM-41) were prepared by a two step modification process started from the hydrothermal synthesis of mesoporous spherical silica particles. 3-(triethoxysilyl)propylsuccinic anhydride (TEPSA) was immobilized over spherical MCM-41 after the surfactant removal by calcination and the proceeding hydrolysis shaped the DA-MCM-41. The synthesized materials were well characterized by various spectroscopic analyses. As a potential application, DA-MCM-41 was effectively utilized for the removal of Fe3+ from aqueous solutions containing various metal ions. The adsorption using DA-MCM-41 was found to have 100% mole and weight selectivities for Fe3+ from aqueous solution containing Cr3+, Mn2+, Fe3+, Co2+, Ni2+, Cu2+, Zn2+, Cd2+ and Pb2+ ions at pH 2, 3, 4 and 5. The material also exhibited 100% mole and weight selectivities for Fe3+ from metal ion mixture containing Li+, Na+, Ca2+ and Mg2+ along with the previously mentioned heavy metals at pH 2 and 3. Interestingly, at pH 4, 5 and 6 the alkali and alkaline earth metals adversely affected the mole and weight selectivities of Fe3+ ions. The reusability test revealed that the DA-MCM-41 can recycle for at least five consecutive cycles without losing the adsorption ability considerably. Also the ligand has excellent adsorption and binding abilities towards Fe3+ from the mixture.
    Full-text · Article · Aug 2015 · Journal of Environmental Chemical Engineering
  • Source
    [Show abstract] [Hide abstract]
    ABSTRACT: Radiation induced graft polymerization on polymeric matrix followed by functionalization is widely accepted for the preparation of metal adsorbents. In this paper, a pre-irradiation method was used for emulsion graft polymerization of 4-hydroxybutyl acrylate glycidylether (4-HB) onto polyethylene/polypropylene (PE/PP) nonwoven fabric. The degree of grafting (D g) which can be calculated by weight increment was determined as a function of reaction time, irradiation dose, and monomer concentration. After 30 kGy irradiation, with 4-HB concentration of 5%, surfactant Span 20 of 0.5% at 40˚C for 2 h, the trunk polymer was made grafted at a D g of 135%. 4-HB-grafted PE/PP nonwoven fabric was modified by ethylenediamine (EDA) in isopropyl alcohol (IPA) as a solvent at 60˚C. With a D g of 135%, the amine group density of the adsorbent is 2.8 mmol/g. The adsorption test was carried out by batch experiment in several metal ion solutions, and the removal ratio from the EDA modified adsorbent of the metal ions is in the order of Cu 2+ > Pb 2+ > Zn 2+ > Ni 2+ > Li + . Compared with glycidyl methacrylate (GMA) which is a typical functional monomer for graft po-lymerization, 4-HB-grafted adsorbent exhibited not only better mechanical property but also higher adsorption capac-ity of Cu 2+ and Pb 2+ .
    Preview · Article · Jan 2011 · Materials Sciences and Applications
  • [Show abstract] [Hide abstract]
    ABSTRACT: Using natural maifan stone as a raw material, a kind of Pb2+ adsorption material was prepared by chemical and heat treatment composite modification method. The modified maifan stones were characterized by X-ray fluorescence spectrometer (XRF) and scanning electronic microscope (SEM). Moreover, the relationships between the absorption rates of Pb2+ with the maifan stone contents, contact time and the initial pH value of the lead nitrate solution were analyzed. The experiment results show that the composite modified maifan stone, which was prepared with heat treatment modification for 0.8 h at 380°C after the chemical modification for 24 h with 2 mol/L sodium chloride solutions, increased significantly in porosity, contact area and absorption properties of Pb2+. And then the adsorption rate of Pb2+ of the composite modified maifan stone was the best and up to 94.5%, at the condition of the initial Pb2+ concentration=50 mg/L, the pH value of the lead nitrate solution =6.0, the maifan stone content=45 g/L, and the contact time=35 min.
    No preview · Article · Jan 2011
Show more