Tropical Agricultural Research Vol. 30 (4): 117 – 123 (2019)
Short Communication
117
Degradation of Unplasticised Poly Vinyl Chloride Based Engineering
Products Upon Exposure to Ultra Violet Radiation
K. G. Alahapperuma and A. M. P. B. Samarasekara1*
Department of Materials Science and Engineering
University of Moratuwa
Sri Lanka
ABSTRACT: Poly vinyl chloride (PVC) is considered as a widely used polymer for various
applications. It is durable, inexpensive and resistant to heat, water and chemicals. Additives
such as lubricants, heat stabilizers, plasticizers, impact modifiers, fillers and ultra violet (UV)
stabilizers enhance its durability and make it suitable for a range of applications. PVC is used
for automobile and other sectors in products ranging from piping and siding, blood bags and
tubing, to wire and cable insulation applications. Poly vinyl chloride exhibits high sensitivity
to UV rays and it is a life time deciding factor specially in outdoor applications. This study
was conducted to analyse the degradation behavior of PVC under the UV environment.
Commercially available 32mm PNT7 unplasticised poly vinyl chloride (uPVC) pipes were
selected for this research. Initially, tensile strength, elongation, hardness and water
absorption properties were analysed. Ultra violet ray exposure test was performed for PVC
samples to evaluate the photo-degradation behavior at selected UV exposure time periods.
Tensile strength, elongation, hardness, water absorption properties and visual inspection tests
were performed after the UV exposure test. Scanning electron microscopic images and
differential thermal analysis were also used to analyze the degradation behavior. It was
indicated a slight reduction of tensile strength, percentage elongation and hardness of samples
with increase of UV exposure time. Scanning electron microscopic images of products showed
degraded features after UV exposure test. This study revealed that uPVC based products are
resistant to photodegradation by UV rays.
Keywords: Photodegradation, UV, uPVC, degradation
INTRODUCTION
Polymers are high molecular weight materials or macromolecules made up of many repeating
chemical units. The term polymer can be defined as a macromolecule with high molecular
mass arising due to the joining of large number of smaller molecules called monomers. A
different monomer or combination of monomers is used to manufacture each different type or
family of polymers. There are many polymers around us that are so familiar to us. The
polymers are characterized by variable molecular weight (depending on the source or mode of
synthesis or extraction), low specific gravity, better resistance to erosion and corrosion, insects
or fungi etc. The advantageous aspect of polymeric materials over other materials as per our
property requirements may be soft to rigid or tough, transparent to opaque, light to heavy,
crystalline to amorphous (Samarasekara and Jayasuriya, 2014).
1 Department of Materials Science and Engineering, University of Moratuwa, Sri Lanka
* Corresponding author: banduamp@gmail.com
This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits
unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
DOI: http://doi.org/10.4038/tar.v30i4.8333
Alahapperuma and Samarasekara
118
Different monomers or combination of monomers are used to manufacture different type or
family of polymers. Polymers are classified based on their origin as natural and synthetic
polymers. Natural polymers are the ones which are isolated from the natural sources. Cotton,
silk, wool, natural rubber etc. belong to this type. There are also polymers modified from these
natural polymers viz., cellophane, cellulose, chitosan, rayon, leather etc. Synthetic polymers
are the polymers based on the low molecular weight compounds such as polyethylene,
polyvinyl chloride (PVC), nylon, bakelite etc. Polymers have a great influence on our society
today (Umadaran et al., 2016).
PVC is one of the mostly used polymeric materials among the plastic materials used today
(Geyer et al., 2017). It is mixed with plasticizers that soften the plastic so that it is more pliable.
If plasticizers were not added, the plastic would be hard and brittle. Some of the plasticizers
used in vinyl plastics are phthalate esters. These esters are volatile compounds of low
molecular weight (Wahl et al., 1999). PVC is used extensively across a broad range of
industrial, technical and everyday applications including widespread use in building, transport,
packaging, electrical/electronic and healthcare applications. PVC is a very durable and long-
lasting material which can be used in a variety of applications, either rigid (uPVC) form or
flexible (PPVC) (Titow, 2012). The original properties of PVC change due to different
environmental factors and these changes lead to a decrease in the polymer’s molecular weight
and physical and chemical properties. Ultraviolet radiation is one source that causes changes
in the molecular structure of PVC. Under the influence of incident energetic radiation, photo-
chemical processes of PVC occur such as chain scission. These changes decrease the
performance of PVC based products and ultimately fracture occurred
(Hawkins,1984).Therefore, it is necessary to analyse the degradation behavior of PVC under
the UV environment. The objective of this research is to analyse the photodegradation of PVC
based products by varying the UV exposure time to get an idea of the degradation process
during the service life.
METHODOLOGY
Commercially available 32 mm uPVC PNT7 pipes (five samples) were selected for this
analysis.
Characterization of UPVC pipes
The UPVC pipes were characterized using images taken Scanning Electron Microscope
(SEM), FTIR spectroscopic techniques and Thermogravimectric Analysis (TGA).
Morphological investigation of UPVC pipes
The surface morphology of UPVC pipes were investigated by SEM (CARLZIESS EBO –
18) before and after the UV exposure test.
Thermogravimetric analysis (TGA)
Thermal stability of the PVC samples was determined by TGA analysis. The sample was
placed in an instrument and heated with rate of 10°C/min at the temperature range between
25 °C - 600 °C under high purity nitrogen environment using TA Instruments-SDT Q600
machine.
Degradation of Unplasticised Poly Vinyl Chloride
119
FTIR spectroscopy
The original and degraded samples were investigated by FTIR spectroscopy using a BRUKER
Alpha-E spectrophotometer. The samples were investigated under ATR mode of the
spectrometer. The FTIR spectra of the samples were obtained in the transmittance mode in the
range of 4000-500cm-1.
Testing of samples
Initially, original tensile strength, percentage elongation, hardness (Shore D) and water
absorption properties were measured. After that prepared samples were subjected to the UV
exposure test under the standard conditions. Seven set of samples were removed from the UV
chamber at different time intervals of 24, 48, 72, 96, 120, 144 and 168 hours. Tensile strength,
percentage elongation, hardness, water absorption properties and visual inspection tests were
done after the UV exposure treatment. Additionally, FTIR spectroscopy, TGA analysis and
scanning electron microscopic (SEM) images were also obtained. Obtained properties were
compared with the properties of original (reference) set of samples. Accelerated UV exposure
test was performed as per ISO: 4582 standards. Tensile properties, hardness and water
absorption properties were performed under ASTM D 638, ASTM D 2240 and ISO 62
standards respectively. All tests were performed for the reference sets of samples under
mentioned standard conditions. Results of each test obtained after different exposure time to
UV were compared with the corresponding test results of reference samples.
RESULTS AND DISCUSSION
Characterization of UPVC samples
Morphological investigation
Figure 1. SEM images of (a) reference sample (b) after exposing to UV for 168 hours.
In comparison to reference sample, few degraded signs were found in the SEM image of the
specimen exposed to UV for 168 hours (Figure 1) indicating the surface deterioration due to
photo-degradation during the UV exposure test.
(a)
(
b
)
Alahapperuma and Samarasekara
120
Analysis of FTIR spectra
Figure 2. FTIR spectrums of reference sample and samples exposed to UV up to 168
hours.
According to the Figure 2, the FTIR spectrums of reference sample and samples exposed to
UV for 168 hours did not show the significant structural changes due to UV exposure.
Thermogravimetric analysis
Thermal analysis test results showed that degradation of the reference sample started at 253 0C
and degraded sample after 168 hours exposed to UV showed the same property at 250.1 0C.
Degraded sample indicated slightly lower thermal stability than the reference sample,
indicating internal structural break down due to photo-degradation.
Analysis of Mechanical Properties
1. Tensile Strength
Tensile test results in Figure 3, showed the gradual reduction of tensile strength with increase
of UV exposure time. Gradual reduction of tensile strength of samples may be due to the
reduction of molecular-chain stiffness, caused by chain scissions due to UV attack.
Degradation of Unplasticised Poly Vinyl Chloride
121
Figure 3. Tensile strength of reference sample and variation with exposure time UV.
2. Elongation at Break
Figure 4. Relative elongation of sample with exposure time of UV.
Test results of percentage elongation at break also reduced somewhat gradually and slightly
with the increase of UV exposure time (Figure 4). The causes of reduction of tensile strength
could have also attributed for a gradual reduction in the elongation of sample. During the
degradation, structure becomes embrittled and molecular weight reduced.
3. Hardness Properties
According to the Figure 5, there is a gradual reduction of hardness with increase of UV
exposure time. Reduction of hardness may be due to the reduction of structural stiffness or
increase of surface softness caused by the degradation process.
Alahapperuma and Samarasekara
122
Figure 5. Hardness of sample with exposure time of UV.
4. Water Absorption Properties
Figure 6 indicated that there is a gradual increase of water absorption with increase of UV
exposure time. This increase could be due to the formation of surface cavities or cracks, due
to the formation of loose surface layer during the degradation process.
Figure 6. Water absorption of sample with exposure time of UV.
CONCLUSIONS
According to the experimental results, it can be concluded that tested samples did not show
significant mechanical property variation after the photodegradation. However, there were
surface morphological changes and reduction of thermal stability of the product due to
photodegradation process.
Degradation of Unplasticised Poly Vinyl Chloride
123
REFERENCES
Geyer, R., Jambeck, J.R. and Law, K.L. (2017). Production, use, and fate of all plastics ever
made. Science advances. 3(7), e1700782.
Hawkins, W.L. (1984). Polymer degradation. pp 3-34. In: Harwood, H. J. (Ed.) Polymer
Degradation and Stabilization. Springer, Berlin, Heidelberg.
Samarasekara, A.M.P.B. and Jayasuriya, E.A.P.C.D. (2014). February. Synthesis of
Biodegradable Polyolefins Based Polymer Composites Using Degradable Natural Materials.
In Proceedings of International Forestry and Environment Symposium. 18.
Titow, M.V. (2012). PVC technology. Springer Science & Business Media.
Umadaran, S., Somasuntharam, P. and Samarasekara, A.M.P.B. (2016). April. Preparation and
characterization of Cellulose and Hemi-Cellulose based degradable composite material using
sugarcane waste. In Moratuwa Engineering Research Conference (MERCon), 2016. 367-372.
IEEE.
Wahl, H.G., Hoffmann, A., Häring, H.U. and Liebich, H.M. (1999). Identification of
plasticizers in medical products by a combined direct thermodesorption–cooled injection
system and gas chromatography–mass spectrometry. Journal of Chromatography. 847(1-2), 1-
7.