Nanocrystalline diamond synthesized from C60. Diam. Relat. Mater. 14(1), 16-22

Bayerisches Geoinstitut, Universität Bayreuth, Universittstrasse 30, 95440 Bayreuth, Germany
Diamond and Related Materials (Impact Factor: 1.92). 11/2010; 14(1):16-22. DOI: 10.1016/j.diamond.2004.06.017


A bulk sample of nanocrystalline cubic diamond with crystallite sizes of 5–12 nm was synthesised from fullerene C60 at 20(1) GPa and 2000 °C using a multi-anvil apparatus. The new material is at least as hard as single crystal diamond. It was found that nanocrystalline diamond at high temperature and ambient pressure kinetically is more stable with respect to graphitisation than usual diamonds.

Download full-text


Available from: Leonid Dubrovinsky
  • Source
    • "They are used as insets in cutting and wear-resistant tools, fabricated by Sumitomo Electric Industries, Ltd. and as anvils in multi-anvil (MA) apparatus and diamond anvil cells (DACs) in Earth and planetary and materials research [9] [10] [11]. Bulk nanocrystalline diamond (NCD), with mechanical properties competing with those of NPDs, was synthesized also from various carbon precursors first in a shape of small (mm-sized) rods [12] [13] [14]. "
    [Show abstract] [Hide abstract]
    ABSTRACT: Here we report the high-pressure and high-temperature synthesis of nanocrystalline diamond (NCD) from glassy carbon balls using a multianvil apparatus. Different chemical compounds were used as the synthesis and pressure transmitting media. A detailed characterization of the synthesized products was performed using optical microscopy, Raman spectroscopy and scanning electron microscopy (SEM). Fully optically transparent nanocrystalline diamond micro-balls and lenses with complete optical transparency and the size of about 15–40 μm were synthesized at a static pressure of 18 GPa in the temperature range of 1850–2000 °С using MgO as a pressure medium.
    Full-text · Article · Feb 2015 · Journal of Crystal Growth
  • Source
    • "Solid line from experimental data shows activation energy (temperatures) needed for the graphite–diamond conversions that fall with the increasing of pressure. activation energy (or needed temperature) [1] [6] [12] [20] [21] "
    [Show abstract] [Hide abstract]
    ABSTRACT: Well-crystallized graphite and high energy ball-milled graphite were treated under 16 GPa and temperatures up to 2500 °C. Our experiments indicated that the ball-milled graphite can completely transform to nano-polycrystalline diamond (NPD) at 2100 °C, while the well-crystallized graphite required 2500 °C. The samples were characterized by X-ray diffraction, optical microscope, scanning electron microscope, and Vickers indenter hardness test. We found that high pressure not only made the conversion of graphite to NPD thermodynamically preferred, but also reduced the needed activation energy barrier. By analyzing thermodynamics and kinetics of the transformation, we suggested a low boundary for NPD forming region based on the phase diagram of carbon, and the formation mechanisms of Nano-polycrystalline diamond.
    Full-text · Article · Jan 2013 · International Journal of Refractory Metals and Hard Materials
  • [Show abstract] [Hide abstract]
    ABSTRACT: The results have been discussed of studying the structure and hardness of polycrystals produced from nanodispersed powders of mixtures of the amorphous carbon phase and nanocrystalline diamond. The initial powders have been synthesized by high-temperature shock compression and sintered at a pressure of 13 GPa and temperatures from 1100 to 2000°C. The sintering has been accompanied by the transformation of amorphous carbon into diamond. As the diamond content of the sample has been increased from 10 to 100%, the hardness increased from 45 to 80 GPa. Keywordsdiamond–amorphous carbon–sintering–nanocrystalline structure–high pressure–hardness
    No preview · Article · Oct 2011 · Journal of Superhard Materials
Show more