During a study of the combustion process of a direct polarity electric arc, a directly proportional dependence of the electric current value on the degree of cold plastic deformation of carbon steel used as an electrode was found. To calculate the value of the electric current during arc burning, in the indicated ratio, it was proposed to replace t...

In comparison with low carbon steels, there is increased interest in the use of aluminium-based alloys as materials for the manufacture of welded structures rolling stock of railway transport. During friction stir welding aluminium-based alloy, against the background of the analysis structural transformations, issues of development hardening proces...

Purpose. The aim of this work is to assess the effect of ferrite grain size of low-carbon steel on the development of strain hardening processes in the area of nucleation and propagation of deformation bands. Methodology. Low-carbon steels with a carbon content of 0.06–0.1% C in various structural states were used as the material for study. The sam...

From an analysis of the dependence complex of carbon steel properties on structural parameters, it was found that for an isostructural state, the influence of austenite grain size on impact strength exceeds the dependence on carbon content. As a result of explaining correlation relationships between individual mechanical characteristics, to evaluat...

Purpose. The main purpose of the work is to determine the peculiarities of the development of recrystallization processes of carbon steel austenite depending on the degree of hot plastic deformation and to develop proposals for improving the structural state of the metal of the railway solid-rolled wheel. Methodology. Two carbon steels of a railway...

The metallographic and fractographic analysis methods were used to study the influence of the cast metal quality on the causes of the destruction of a railway carriage under high dynamic and cyclic loads. As a result of study structure fracture surface of the side frame freight car truck, the detected elements indicate simultaneous presence of fati...

On a fragment of the rim of a railway wheel removed from service, the volume of the metal with non-metallic inclusions located near the tread surface was investigated. The use of the microhardness measurement technique made it possible to establish the nature of strain hardening of carbon steel near non-metallic inclusions. It showed that with a no...

Purpose. The work is aimed to clarify the softening mechanism during the heating of martensite hardened carbon steel, which is of practical importance, especially in the development of the production technology of rolled products with different levels of hardening. Methodology. The samples after martensite hardening were tempered at the temperature...

Purpose. The paper aims at estimation of resource of strength increase for railway wheel disk. Methodology. The material for research was carbon steel of railway wheel containing 0.57%C, 0.65%Si, 0.45%Mn, 0.0029%S, 0,014%P, 0,11%Cr. A railway wheel was heated to the temperatures above and was held at this temperature until the completion of аusteni...

Purpose. Assessing the impact of technological parameters on the properties of the complex in the manufacture of valves with a high level of safety. Methodology. Material for the study was selected alloy steel 20ХГС2. Curing rods with a diameter of 6,5 mm was performed rapid cooling from temperatures of 1080…1100 °C. The heating was carried out in...

Purpose. The purpose of work is an estimation of influence of an electric spark treatment on the state of mouldable superficial coverage of carbon steel. Methodology. The steel of fragment of railway wheel rim served as material for research with chemical composition 0.65% С, 0.67% Mn, 0.3% Si, 0.027% P, 0.028% S. Structural researches were conduct...

Purpose. Explanation of the influence mechanism of ferrite grain size on the fatigue strength of low-carbon steel. Methodology. Material for research is the low-carbon steel with 0.1% of carbon contnent. The different size of ferrite grain was obtained due to varying the degree of cold plastic deformation and temperature of annealing. The estimatio...

Performed modeling studies of the effect of cooling conditions rod at its microstructure, and determined that the temperature rise of wire rod at laying head promotes to formation of a more dispersed structure of the metal.

Purpose. The purpose of work is the possibility estimation of аthermic technologies use of cold-deformed metal softening for elements of railway car body and wheel. Methodology. The material for research is the carbon steel of the wheel rim fragment containing 0.55%С, 0.74%Mn, 0.33%Si, and the steel 20. The wheel steel is studied after heat strengt...