Pablo Moreno- PhD
- investigador at University of Bío-Bío
Pablo Moreno
- PhD
- investigador at University of Bío-Bío
Investigador Centro de Investigación en Tecnologías de la Construcción (CITEC-UBIOBIO)
About
25
Publications
10,845
Reads
How we measure 'reads'
A 'read' is counted each time someone views a publication summary (such as the title, abstract, and list of authors), clicks on a figure, or views or downloads the full-text. Learn more
75
Citations
Introduction
Current institution
Additional affiliations
January 2001 - October 2016
June 2001 - July 2016
June 2002 - June 2016
Publications
Publications (25)
This study aimed to evaluate the effect of water immersion on the release of growth stresses in 17-year-old Eucalyptus nitens logs. A total of 18 of 90 trees evaluated in the field were selected. The average diameter at the height breast of all the trees was 37 cm. The first section of the tree, from the stump to 2.44 m, was used. Three stress leve...
O Pinus radiata (Pinus Radiata D. Don), uma espécie de crescimento rápido no Chile, tem uma resistência mecânica inferior ao de outras coníferas utilizadas como madeira estrutural, mesmo bem abaixo de algumas madeiras chilenas com altas qualidades estruturais. O objetivo desta pesquisa foi estudar o efeito de um tratamento termo-higromecânico do ti...
Resumen Existe una creciente necesidad de llevar a cabo acciones con el fin de utilizar de mejor manera los alimentos y sus residuos, ya que están originando serios problemas de contaminación ambiental, y se desperdician múltiples recursos en su producción, procesamiento y transporte. Los gobiernos e instituciones privadas están abordando el tema c...
Efecto de la granulometría de la partícula de madera sobre las propiedades mecánicas y térmicas en tableros madera-cemento Effect of the wood particle size on the mechanical and thermal properties of wood-cement boards Resumen La tecnología del concreto busca mejorar el rendimiento de las mezclas cementicias bajo un enfoque particular en la ecoefic...
Introduction:
The use of wood-plastic composites (WPCs) has been limited due to their low impact strength and high density compared to natural wood.
Objective:
To characterize the cellular morphology and density of WPCs prepared with virgin and recycled polyethylene, and Pinus radiata wood.
Materials and methods:
The polymer and the foamed WPCs w...
Este es un estudio exploratorio para dar uso a la madera de Eucalyptus urophylla en la elaboración de tableros aglomerados de partículas. Por lo tanto, los objetivos fueron determinar sus propiedades físico-mecánicas y evaluar los resultados bajo norma Alemana Instituto Alemán de Normalización (DIN) y Venezolana Comisión Venezolana de Normas Indust...
Este estudio es una propuesta para dar un aprovechamiento y uso a los residuos industriales delaserrío de la madera de Pinus patula para la elaboración de tableros aglomerados de partículas. Por lotanto, los objetivos fueron manufacturar tableros aglomerados de partículas homogéneos a dos nivelesde densidad, determinar sus propiedades físico-mecáni...
This study is a proposal to generate uses of industrial residues from sawmills of Pinus patula wood for the manufacturing of particleboards. The aims are to manufacture homogeneous particleboards with two density levels, determine their physical and mechanical properties and evaluate the results with German and Venezuelan standards. The average wat...
Based on ASTM standards D 2395-02 and D 143-94, total and normal shrinkage in radial (RS), tangential (TS) and volumetric (VS) directions and the total and normal TS/RS ratio were determined in the plantation woods Acacia mangium Willd., Tectona grandis L.f. and Terminalia amazonia A. Chev. Also, physical properties such as basic specific gravity (...
The objective of the present study was to observe the morphology and characterize the mechanical properties of wood plastic composite foams. Recycled high density polyethylene was mixed with Pinus radiata D. Don (radiata pine) wood fiber of 60 mesh. The fiber concentrations were 15 and 25% by weight. The compounds were foamed with a chemical agent...
The industry agglomerated panels incorporated into its manufacturing process tree species of both conifers and hardwoods, today, many companies operate at half of its production capacity for the continued lack of raw material due to depletion of main species or operational restriction. The main objective of this paper was to determine the technolog...
El objetivo principal de este estudio es determinar la factibilidad tecnológica de Fraxinus americana como materia prima para la fabricación de tableros aglomerados de partículas a dos niveles de densidad teórica (nominal) de 0,600 g/cm3 y 0,800 g/cm3 con adhesivo urea formaldehído al 8% de resinosidad. Las propiedades físicas y mecánicas de los ta...
SUMMARY The main objective of this research was to determine the technological feasibility of Bambusa vulgaris as raw material for the production of particleboard at two levels of theoretical density, of 600 kg/m3 and 800 kg/m3, with formaldehyde urea resin content of 8%. The physical and mechanical properties of the boards were determined accordin...
Twenty five year old Caribbean pine trees grown in an experimental plantation at the Irel Experimental Station, Barinas state, Venezuelan, were used for the manufactured of oriented strand boards (OSB) at two theoretical densities levels of 0.600 and 0.800 g/cm 3 , at 8% formaldehyde urea resin content, 7% ammonium sulphate solution content as the...
Introducción La industria de paneles aglomerados de partículas en Venezuela, tiene restricciones tecnológicas que im-piden el procesamiento de numerosas especies. Por es-ta razón se desaprovechan cerca del 90% de especies, que ya han sido estudiadas y cuya madera presenta ca-racterísticas adecuadas para su incorporación al mer-cado. Se están estudi...
RESUMEN El objetivo principal de esta investigación fue determinar la factibilidad tecnológica de Bambusa vulgaris como materia prima para la fabricación de tableros aglomerados de partículas, a dos niveles de densidad teórica, de 600 kg/m 3 y 800 kg/m 3 , con adhesivo de urea formaldehído al 8 % de resinosidad. Las propiedades físicas y mecánicas...
INTRODUCCIÓN La utilización de paneles en el rubro de la cons-truc-ción ha aumentado considerablemente en los últimos tiempos. Cada vez con mayor intensidad se incorpo-ran tableros contrachapados, enlistonados, de fibra y de partículas a la fabricación de viviendas y otras edificaciones. Los paneles aglomerados, incluidos como forros in-teriores, p...
Mecanografiado Informe de pasantía (Ing. Forestal).-- Universidad de Los Andes, Facultad de Ciencias Forestales y Ambientales, Escuela de Ingeniería Forestal, Mérida, 2004 Incluye bibliografía
Mecanografiado Informe de pasantía (Ing. Forestal)-- Universidad de Los Andes, Facultad de Ciencias Forestales y Ambientales, Escuela de Ingeniería Forestal, Mérida, 2002 Incluye bibliografía
Mecanografiado Informe de pasantía (Ing. Forestal)-- Universidad de Los Andes, Facultad de Ciencias Forestales, Escuela de Ingeniería Forestal, Mérida, 1993 Incluye bibliografía
Mecanografiado Informe de Pasantía (Ing. Forestal)-- Universidad de Los Andes, Facultad de Ciencias Forestales y Ambientales, Escuela de Ingeniería Forestal, Mérida, 2001 Incluye bibliografía
Mecanografiado Informe de pasantías (Ing. Forestal)-- Universidad de Los Andes, Facultad de Ciencias Forestales y Ambientales, Escuela de Ingeniería Forestal, Mérida, 2007 Incluye bibliografía
Mecanografiado Informe de Pasantía (Ing. Forestal).-- Universidad de Los Andes, Facultad de Ciencias Forestales y Ambientales, Escuela de Ingenieria Forestal, Laboratorio Nacional de Productos Forestales, Sección de Aglomerados, Mérida, 2003 Incluye bibliografía
Mecanografiado Tesis (Magister Scientiae)-- Universidad de Los Andes, Facultad de Ciencias Forestales y Ambientales, Centro de Estudios Forestales y Ambientales de Postgrado, Mérida, 2001 Incluye bibliografía
Questions
Question (1)
I am working with nanoparticles of Copper. I have a sample of nanoparticles of copper, according to the company has 80 nm of diameters, I am using the UP200St ultrasonic to disperse the nanoparticles of copper to characterize them through the SEM and I have not been able to disperse to obtain diameters inferior to 100nm. To disperse I used 1 mg de nanoparticle Cu in 50 ml of ethanol, a dispersion time of 40 min. When the solution is heated I cool with ice. I would like to know if I am using the proper procedure?. I could not disperse copper well.