(a) Nanoepoxy resin; (b) nanostitchingyarn; (c) nanoprepregfabric surface (Optic microscope, magnification x4, x4, x1, respectively).
Contexts in source publication
Context 1
... this reason, we decreased the MNCNT ratio and increased the stirring time in ultrasonic mixing. Therefore, the size of the agglomeration of carbon nanotubes decreased to 30-80 microns in the epoxy ( Figure 1(a)). The MWCNT added epoxy was applied to the stitching yarn (Figure 1(b)) and fabric (Figure 1(c). ...
Context 2
... the size of the agglomeration of carbon nanotubes decreased to 30-80 microns in the epoxy ( Figure 1(a)). The MWCNT added epoxy was applied to the stitching yarn (Figure 1(b)) and fabric (Figure 1(c). ...
Context 3
... the size of the agglomeration of carbon nanotubes decreased to 30-80 microns in the epoxy ( Figure 1(a)). The MWCNT added epoxy was applied to the stitching yarn (Figure 1(b)) and fabric (Figure 1(c). ...
Context 4
... started by selecting 0.5% (weight %) ratio for the MWCNTs as an initial condition. Later on, a large agglomeration (about 200-300 microns) of nanotubes was found in the epoxy. Extensive studies were conducted to decrease the size of the agglomeration of the nanotubes. For this reason, we decreased the MNCNT ratio and increased the stirring time in ultrasonic mixing. Therefore, the size of the agglomeration of carbon nanotubes decreased to 30-80 microns in the epoxy ( Figure 1(a)). The MWCNT added epoxy was applied to the stitching yarn (Figure 1(b)) and fabric (Figure ...
Context 5
... started by selecting 0.5% (weight %) ratio for the MWCNTs as an initial condition. Later on, a large agglomeration (about 200-300 microns) of nanotubes was found in the epoxy. Extensive studies were conducted to decrease the size of the agglomeration of the nanotubes. For this reason, we decreased the MNCNT ratio and increased the stirring time in ultrasonic mixing. Therefore, the size of the agglomeration of carbon nanotubes decreased to 30-80 microns in the epoxy ( Figure 1(a)). The MWCNT added epoxy was applied to the stitching yarn (Figure 1(b)) and fabric (Figure ...
Context 6
... started by selecting 0.5% (weight %) ratio for the MWCNTs as an initial condition. Later on, a large agglomeration (about 200-300 microns) of nanotubes was found in the epoxy. Extensive studies were conducted to decrease the size of the agglomeration of the nanotubes. For this reason, we decreased the MNCNT ratio and increased the stirring time in ultrasonic mixing. Therefore, the size of the agglomeration of carbon nanotubes decreased to 30-80 microns in the epoxy ( Figure 1(a)). The MWCNT added epoxy was applied to the stitching yarn (Figure 1(b)) and fabric (Figure ...