In this study, X-ray diffraction (XRD) analysis showed the amorphous nature of the Co60Fe20Yb20 films deposited at room temperature (RT), 100 °C, and 200 °C. The body-centered cubic (BCC) CoFe (110) characteristic peak was visible at 44.7° after annealing films of 40 nm and 50 nm at 300 °C. The highest alternating current magnetic susceptibility (χ...
Context in source publication
Context 1
... thickness effect causes a rise in χac as thickness increases. The maximum χac of annealed CoFeYb thin films was larger than that at RT. Table 2 shows the maximum χac for the ideal resonance frequency (fres) under four different situations. The greatest χac had the highest spin sensitivity at the fres [27,28]. ...Similar publications
In this work, AlCr and AlCrFe coatings were deposited via magnetron sputtering on technical substrates of carbon steel C45 and titanium grade 2. The coatings feature an amorphous structure, a thickness of 3–4 μm, and are uniform in terms of thickness and chemical composition. No major defects were visible at the interface; however, there is no diff...