In this study, X-ray diffraction (XRD) analysis showed the amorphous nature of the Co60Fe20Yb20 films deposited at room temperature (RT), 100 °C, and 200 °C. The body-centered cubic (BCC) CoFe (110) characteristic peak was visible at 44.7° after annealing films of 40 nm and 50 nm at 300 °C. The highest alternating current magnetic susceptibility (χ...
Context in source publication
Context 1
... structure, magnetic properties, electrical properties, mechanical properties, contact angle adhesion efficiency, and optical characteristics of Co60Fe20Yb20 thin films with varying thicknesses and heat treatments were all measured in this work. In previous research, the as-deposited and post-annealing Co60Fe20Y20 films were compared with Co60Fe20Yb20 films for their magnetic, optic, and adhesive properties, as mentioned in Table 1 [21]. ...Similar publications
In this work, AlCr and AlCrFe coatings were deposited via magnetron sputtering on technical substrates of carbon steel C45 and titanium grade 2. The coatings feature an amorphous structure, a thickness of 3–4 μm, and are uniform in terms of thickness and chemical composition. No major defects were visible at the interface; however, there is no diff...