HAADF images and EDS line profiles for precipitates P11 and P91 along different paths. The points in the curves have been fitted using c-splines. The key for both HAADF images is presented below the HAADF image of P11. HAADF images have been acquired using the TIA v4.2 (FEI www.fei.com) software. Fiji v2.1.0/1.53c (https://fiji.sc), gnuplot v5.4 (http://www.gnuplot.info) and Microsoft PowerPoint have been used to prepare this image.

HAADF images and EDS line profiles for precipitates P11 and P91 along different paths. The points in the curves have been fitted using c-splines. The key for both HAADF images is presented below the HAADF image of P11. HAADF images have been acquired using the TIA v4.2 (FEI www.fei.com) software. Fiji v2.1.0/1.53c (https://fiji.sc), gnuplot v5.4 (http://www.gnuplot.info) and Microsoft PowerPoint have been used to prepare this image.

Source publication
Preprint
Full-text available
Precipitates in an austenitic stainless steel fabricated via any Additive Manufacturing (AM), or 3D printing, technique have been widely reported to be only Mn-Si-rich oxides. However, via Transmission Electron Microscopy (TEM) studies on a 316L stainless steel, we show that non-oxide precipitates (intermetallics, sulfides, phosphides and carbides)...

Similar publications

Article
Full-text available
Precipitates in an austenitic stainless steel fabricated via any Additive Manufacturing (AM), or 3D printing, technique have been widely reported to be only Mn-Si-rich oxides. However, via Transmission Electron Microscopy (TEM) studies on a 316L stainless steel, we show that non-oxide precipitates (intermetallics, sulfides, phosphides and carbides)...
Article
Full-text available
The fluidity of A356 aluminum alloy was experimentally determined at the melt temperatures and vacuum degrees by a series of suction fluidity tests. In order to achieve different cooling rates during the test, quartz tubes, as well as stainless steel tubes, were employed as the fluidity channels. As the melt temperature increased from 650 to 730 ∘C...
Conference Paper
Full-text available
AA7075 matrix bimetal composites reinforced with 304 stainless steel (SS) were manufactured by melt infiltration casting technique. A preform, made by assembling 304 SS shavings under 220 MPa pressure, was infiltrated by molten AA7075 alloy under vacuum atmosphere during this process. The preform was preheated for 10 min before infiltration to avoi...