Figure - available from: Advanced Materials
This content is subject to copyright. Terms and conditions apply.
Characterization of Na2O‐based high capacity presodiation agent. a) Voltage profile for (Na2O + NiO) composite cathode at 10 mA g⁻¹ with a 4.5 V upper cutoff potential; the inset shows the pure Na2O cathode capacity (<15 mAh g⁻¹) at cutoff 4.5 V. b) Schematic illustration of the preparation procedure of NNO composite presodiation agent by high‐energy ball milling. c) sXRD pattern and d) NPD pattern of NNO presodiation agent and the results of fitting via Rietveld refinement. e) The density of states (DOS) of Na2O (top) and Ni–Na2O (bottom). f) Gibbs free energy diagrams during the pure Na2O and Ni–Na2O decomposition process.
Source publication
Compensating for the irreversible loss of limited active sodium (Na) is crucial for enhancing the energy density of practical sodium‐ion batteries (SIBs) full‐cell, especially when employing hard carbon anode with initially lower coulombic efficiency. Introducing sacrificial cathode presodiation agents, particularly those that own potential anionic...
Similar publications
In order to improve the specific capacity of intercalation electrodes for sodium-ion batteries, it is necessary to identify materials capable of storing Na⁺ ions by activating multi-electron redox reactions. Herein, we report a NaFeVPO4(SO4)2 compound as a multi-electron electrode that combines the most abundant Fe and V ions, having multiple oxida...
Citations
More and more basic practical application scenarios have been gradually ignored/disregarded, in fundamental research on rechargeable batteries, e.g. assessing cycle life under various depths‐of‐discharge (DODs). Herein, although benefit from the additional energy density introduced by anionic redox, we critically revealed that lithium‐rich layered oxide (LRLO) cathodes present anomalously poor capacity retention at low‐DOD cycling, which is essentially different from typical layered cathodes (e.g. NCM), and pose a formidable impediment to the practical application of LRLO. We systemically demonstrated that DOD‐dependent capacity decay is induced by the anionic redox and accumulation of oxidized lattice oxygen (On‐). Upon low‐DOD cycling, the accumulation of On‐ and the persistent presence of vacancies in the transition metal (TM) layer intensified the in‐plane migration of TM, exacerbating the expansion of vacancy clusters, which further facilitated detrimental out‐of‐plane TM migration. As a result, the aggravated structural degradation of LRLO at low‐DOD impeded reversible Li+ intercalation, resulting in rapid capacity decay. Furthermore, prolonged accumulation of On‐ persistently corroded the electrode‐electrolyte interface, especially negative for pouch‐type full‐cells with the shuttle effect. Once the “double‐edged sword” effect of anionic redox being elucidated under practical condition, corresponding modification strategies/routes would become distinct for accelerating the practical application of LRLO.
More and more basic practical application scenarios have been gradually ignored/disregarded, in fundamental research on rechargeable batteries, e.g. assessing cycle life under various depths‐of‐discharge (DODs). Herein, although benefit from the additional energy density introduced by anionic redox, we critically revealed that lithium‐rich layered oxide (LRLO) cathodes present anomalously poor capacity retention at low‐DOD cycling, which is essentially different from typical layered cathodes (e.g. NCM), and pose a formidable impediment to the practical application of LRLO. We systemically demonstrated that DOD‐dependent capacity decay is induced by the anionic redox and accumulation of oxidized lattice oxygen (Oⁿ⁻). Upon low‐DOD cycling, the accumulation of Oⁿ⁻ and the persistent presence of vacancies in the transition metal (TM) layer intensified the in‐plane migration of TM, exacerbating the expansion of vacancy clusters, which further facilitated detrimental out‐of‐plane TM migration. As a result, the aggravated structural degradation of LRLO at low‐DOD impeded reversible Li⁺ intercalation, resulting in rapid capacity decay. Furthermore, prolonged accumulation of Oⁿ⁻ persistently corroded the electrode‐electrolyte interface, especially negative for pouch‐type full‐cells with the shuttle effect. Once the “double‐edged sword” effect of anionic redox being elucidated under practical condition, corresponding modification strategies/routes would become distinct for accelerating the practical application of LRLO.