    ABSTRACT: As the final step in the series of studies on the development of Chinese wattle tannin adhesives, factory trials were carried out in order to evaluate the feasibility of this technology for producing exterior grade plywood in China. More than 1 tonne of wattle tannin adhesives were formulated using PF and PUF resins developed as cross-linking agents. A total of 460 sheets of plywood (1830 × 915 × 9 mm) were produced during four and a quarter working shifts totalling 34 working hours in the plywood factory. The results of gluebond assessments strongly indicate that the technology developed would be extremely feasible for application in the Chinese plywood manufacturing industry. In früheren Arbeiten wurde die Herstellung von Tanninklebern aus Akazienextrakten (Acacia mearnsii) beschrieben. Zum Abschluß dieser Entwicklung wurde ein Großversuch im industriellen Maßstab durchgeführt, um damit die Eignung dieses Klebers für die Sperrholzproduktion in China abzuschätzen. Aus Akazientannin wurde über eine Tonne Tanninkleber mit PF und PUF als Vernetzer hergestellt. Damit wurden insgesamt 460 Sperrholzblätter (1830 × 915 × 9 mm) während viereinviertel Arbeitsschichten bzw. 34 Arbeitsstunden in einem Sperrholzbetrieb hergestellt. Die Festigkeitsprüfungen ergaben, daß die angewandte Technologie sich hervorragend zur Sperrholzherstellung in China eignet.
    Holz als Roh- und Werkstoff 01/1996; 54(2):89-91. · 0.89 Impact Factor
  • L. Zhao, B. Cao, F. Wang, Y. Yazaki
    European Journal of Wood and Wood Products. 01/1996; 54(2):89-91.
  • L. Zhao, B. Cao, F. Wang, Y. Yazaki
    European Journal of Wood and Wood Products. 01/1995; 53(1):117-122.
  • L. Zhao, B. Cao, F. Wang, Y. Yazaki
    [Show abstract] [Hide abstract]
    ABSTRACT: Chinese wattle tannin adhesives were prepared in conjunction with the preparation of phenol-formaldehyde (PF) and phenolurea-formaldehyde (PUF) resins as crosslinking agents which can be substitutes for expensive paraformaldehyde. Adhesive formulations and gluing conditions were examined by preparing laboratory plywoods (300×300 mm). Based on the results obtained, plywoods (600×600 mm) ofTilia species and ofPinus massoniana were prepared using wattle tannin adhesives in pilot plant trials. The gluing results revealed that the tensile strength of the plywood can meet the requirements of the Chinese Standard GB9846.4-88 for exterior grade plywood. Tannin aus chinesischer Akazie wurde in Phenolformaldehydharzen (PF) und Phenol-Harnstoff-Formaldehydharzen (PUF) als Vernetzungsmittel eingesetzt, um Paraformaldehyd zu substituieren. Klebermischungen und Leimbedingungen wurden anhand von Labor-Sperrholzplatten (300×300 mm) überprüft. Aufgrund dieser Testergebnisse wurden Sperrholzplatten aus Linden- und Kiefernholz mit den Abmessungen 600×600 mm unter Industriebedingungen mit dem Akazientannin-Kleber hergestellt. Die Zugfestigkeit der Platten entsprach dem Chinesischen Standard für die Außenverwendung von Sperrholz.
    Holz als Roh- und Werkstoff 01/1995; 53(2):117-122. · 0.89 Impact Factor
  • L. Zhao, B. Cao, F. Wang, Y. Yazaki
    [Show abstract] [Hide abstract]
    ABSTRACT: Wattle tannin adhesives were successfully formulated from tannin extracts, which were commercially produced from black wattle (Acacia mearnsii) bark in China. Using the Chinese wattle tannin adhesives a total of 153 plywood panels were prepared in order to study effects of pH, paraformaldehyde, glue spread, hot pressing temperature and time, and closed assembly time on bonding strength and their bonding quality was assessed according to the Chinese Standard for exterior grade plywood. Statistical analysis results revealed that Chinese wattle tannin can be used for producing exterior grade plywood under Chinese plywood factory conditions. One of the specific characteristics of these Chinese wattle tannin adhesives was that their use resulted in plywood of high quality bonding over the wide range of closed assembly time from 30 minutes to 16 hours. These Chinese wattle tannin adhesives have a great potential for commercialization in China. Aus Akazientannin, das in China kommerziell aus der Rinde von Acacia mearnski extrahiert wird, konnten geeignete Sperrholz-Kleber gewonnen werden. Mit diesem Kleber wurden 153 Sperrholzplatten hergestellt. Daran wurde der Einfluß von pH, Paraformaldehydmenge, Leimverteilung, Preßtemperatur und Preßzeit sowie der Schließzeit auf die Festigkeit der inneren Bindungen untersucht. Die Prüfung erfolgte nach dem chinesischen Standard für Außenverwendung von Sperrholz. Statistisch gesichert erwies sich das Akazientannin als geeignet zur Herstellung von Sperrholz für die Außenverwendung. Eine characteristische Eigenschaft dieser Kleber war, daß über einen weiten Bereich von Schließzeiten (von 30 min. bis 16h) Sperrholz von hoher Bindungsqualität hergestellt werden kann. In China dürften diese Kleber einen hohen Marktwert erreichen.
    Holz als Roh- und Werkstoff 01/1994; 52(2):113-118. · 0.89 Impact Factor