[show abstract]
[hide abstract]
ABSTRACT: The polysaccharide ulvan, composed of sulphated rhamnose, glucoronic and iduronic acids was used to produce polymeric membranes by solvent casting. As ulvan is soluble in water, a cross-linking step was necessary to render the membrane insoluble in water and stable at physiological conditions. Cross-linked ulvan membranes were characterized by FTIR, SEM, swelling behaviour was investigated and the mechanical performance assessed by quasi-static tensile testing. Furthermore, the ability and mechanism of sustained release of a model drug from ulvan membranes was investigated. Produced membranes revealed remarkable ability to uptake water (up to ∼1800% of its initial dry weight) and increased mechanical performance (1.76 MPa) related with cross-linking. On the other hand, medicated ulvan dressings demonstrate the potential as drug delivery devices. Using a model drug we have observed an initial steady release of the drug - of nearly 49% - followed by slower and sustained release up to 14 days. The properties of ulvan membranes herein revealed suggest a great potential of this natural sulphated polysaccharide as a wound dressing.
International journal of pharmaceutics 04/2012; 426(1-2):76-81. · 2.96 Impact Factor
-
[show abstract]
[hide abstract]
ABSTRACT: Native bone extracellular matrix (ECM) is a complex hierarchical fibrous composite structure, resulting from the assembling of collagen fibrils at several length scales, ranging from the macro to the nanoscale. The combination of nanofibers within microfibers after conventional reinforcement methodologies seems to be a feasible solution to the rational design of highly functional synthetic ECM substitutes. The present work aims at the development of bone ECM inspired structures, conjugating electrospun chitosan (Cht) nanofibers within biodegradable polymeric microfibers [poly(butylene succinate)-PBS and PBS/Cht], assembled in a fiber mesh structure. The nanofibers-reinforced composite fiber mesh scaffolds were seeded with human bone marrow mesenchymal stem cells (hBMSCs) and cultured under osteogenic differentiation conditions. These nanofibers-reinforced composite scaffolds sustained ECM deposition and mineralization, mainly in the PBS/Cht-based fiber meshes, as depicted by the increased amount of calcium phosphates produced by the osteogenic differentiated hBMSCs. The osteogenic genotype of the cultured hBMSCs was confirmed by the expression of osteoblastic genes, namely Alkaline Phosphatase, Osteopontin, Bone Sialoprotein and Osteocalcin, and the transcription factors Runx2 and Osterix, all involved in different stages of the osteogenesis. These data represent the first report on the biological functionality of nanofibers-reinforced composite scaffolds, envisaging the applicability of the developed structures for bone tissue engineering.
Tissue Engineering Part A 12/2010; 16(12):3599-609. · 4.64 Impact Factor
-
[show abstract]
[hide abstract]
ABSTRACT: Melt blends of chitosan and biodegradable aliphatic polyester have been physically and biologically studied, presenting great potential for biomedical applications. Structurally, poly(butylene succinate)-chitosan (PBS/Cht) composite scaffolds are covered by a thin PBS layer, preventing the desired interaction of cells/tissues with the chitosan particules. In the present work, a selective and controlled ablation of this skin layer was induced by UV laser processing. X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS) data demonstrated an increment of chitosan components and others resulting from the laser ablation process. The biological activity (i.e. cell viability and proliferation) on the inner regions of the composite scaffolds is not significantly different from those of the external layer, despite the observed differences in surface roughness (determined by interferometric optical profilometry) and wettability (water contact angle). However, the morphology of human osteoblastic cells was found to be considerably different in the case of laser-processed samples, since the cells tend to aggregate in multilayer columnar structures, preferring the PBS surface and avoiding the chitosan-rich areas. Thus, UV laser ablation can be considered a model technique for the physical surface modification of biomaterials without detrimental effects on cellular activity.
Journal of Tissue Engineering and Regenerative Medicine 08/2010; 4(6):444-53. · 3.28 Impact Factor
-
[show abstract]
[hide abstract]
ABSTRACT: Utilize the dual composition strategy to increase the pore size and solve the low cell infiltration capacity on random nanofiber meshes, an intrinsic limitation of electrospun scaffolds for tissue engineering applications.
Polycaprolactone and poly(ethylene oxide) solutions were electrospun simultaneously to obtain a dual composition nanofiber mesh. Selective dissolution of the poly(ethylene oxide) nanofiber fraction was performed. The biologic performance of these enhanced pore size nanofibrous structures was assessed with human osteoblastic cells.
The electrospun nanofiber meshes, after the poly(ethylene oxide) dissolution, showed statistically significant larger pore sizes when compared with polycaprolactone nanofiber meshes with a similar polycaprolactone volume fraction. This was also confirmed by interferometric optical profilometry. Using scanning electron microscopy and laser scanning confocal microscopy, it was observed that osteoblastic cells could penetrate into the nanofibrous structure and migrate into the opposite and unseeded side of the mesh.
An electrospun mesh was created with sufficient pore size to allow cell infiltration into its structure, thus resulting in a fully populated construct appropriate for 3D tissue engineering applications.
Nanomedicine 06/2010; 5(4):539-54. · 5.05 Impact Factor
-
[show abstract]
[hide abstract]
ABSTRACT: A critical aspect in the development of biomaterials is the optimization of their surface properties to achieve an adequate cell response. In the present work, electrospun polycaprolactone nanofiber meshes (NFMs) are treated by radio-frequency (RF) plasma using different gases (Ar or O(2)), power (20 or 30 W), and exposure time (5 or 10 min). Morphological and roughness analysis show topographical changes on the plasma-treated NFMs. X-ray photoelectron spectroscopy (XPS) results indicate an increment of the oxygen-containing groups, mainly --OH and --C==O, at the plasma-treated surfaces. Accordingly, the glycerol contact angle results demonstrate a decrease in the hydrophobicity of plasma-treated meshes, particularly in the O(2)-treated ones. Three model cell lines (fibroblasts, chondrocytes, and osteoblasts) are used to study the effect of plasma treatments over the morphology, cell adhesion, and proliferation. A plasma treatment with O(2) and one with Ar are found to be the most successful for all the studied cell types. The influence of hydrophilicity and roughness of those NFMs on their biological performance is discussed. Despite the often claimed morphological similarity of NFMs to natural extracellular matrixes, their surface properties contribute substantially to the cellular performance and therefore those should be optimized.
Small 03/2009; 5(10):1195-206. · 8.35 Impact Factor
-
[show abstract]
[hide abstract]
ABSTRACT: Blends of chitosan and biodegradable synthetic aliphatic polyesters (polycaprolactone, poly(butylene succinate), poly[(butylene succinate)-co-adipate], poly[(butylene terephthalate)-co-adipate], and poly(lactic acid)) were injection-molded. These samples were immersed in isotonic solution at 37 degrees C for a period of 60 d. The water uptake and the degradation properties, as measured by the loss in tensile strength, were evaluated as a function of time. In this study, the rate and the equilibrium water uptake were proportional to the amount of chitosan in the blend. The addition of HA to chitosan and polyester significantly reduced the equilibrium water uptake. The water uptake did not follow the classical Fickian phenomena and could be expressed by a two-stage sorption non-Fickian diffusion model. Contact angle measurement was used to quantify the changes in surface hydrophilicity as a function of chitosan and polyester composition. The glycerol contact angle decreased with increasing synthetic components in the blend. The blends and composites also showed increased degradation, as quantified by a loss in their mechanical properties, with increase in natural content. The degradation of properties was directly related to the water uptake of the blends; the higher the water uptake, the higher the degradation. Pure polyesters, while having low water uptake, nevertheless showed significant degradation by a precipitous drop in the strain at break. Among the polyesters, poly(lactic acid) displayed maximum degradation, while polycaprolactone displayed the least.
Macromolecular Bioscience 04/2007; 7(3):354-63. · 3.89 Impact Factor