Biomechanical and biochemical characterization of composite tissue-engineered intervertebral discs.

Center for Tissue Engineering, University of Massachusetts Medical School, Worcester, MA, USA.
Biomaterials (Impact Factor: 8.31). 02/2006; 27(3):362-70. DOI: 10.1016/j.biomaterials.2005.06.042
Source: PubMed

ABSTRACT Composite tissue-engineered intervertebral tissue was assembled in the shape of cylindrical disks composed of an outer shell of PGA mesh seeded with annulus fibrosus cells with an inner core of nucleus pulposus cells seeded into an alginate gel. Samples were implanted subcutaneously in athymic mice and retrieved at time points up to 16 weeks. At all retrieval times, samples maintained shape and contained regions of distinct tissue formation. Histology revealed progressive tissue formation with distinct morphological differences in tissue formation in regions seeded with annulus fibrosus and nucleus pulposus cells. Biochemical analysis indicated that DNA, proteoglycan, and collagen content in tissue-engineered discs increased with time, reaching >50% of the levels of native tissue by 16 weeks. The exception to this was the collagen content of the nucleus pulposus portion of the implants with were approximately 15% of native values. The equilibrium modulus of tissue-engineered discs was 49.0+/-13.2 kPa at 16 weeks, which was between the measured values for the modulus of annulus fibrosus and nucleus pulposus. The hydraulic permeability of tissue-engineered discs was 5.1+/-1.7x10(-14) m2/Pa at 16 weeks, which was between the measured values for the hydraulic permeability of annulus fibrosus and nucleus pulposus. These studies document the feasibility of creating composite tissue-engineered intevertebral disc implants with similar composition and mechanical properties to native tissue.

0 Followers
 · 
104 Views
  • [Show abstract] [Hide abstract]
    ABSTRACT: Because of the limitations of current surgical methods in the treatment of degenerative disc disease, tissue engineered intervertebral discs (TE-IVDs) have become an important target. This study investigated the biochemical and mechanical responses of composite TE-IVDs to dynamic unconfined compression. TE-IVDs were manufactured by floating an injection molded alginate nucleus pulposus (NP) in a type I collagen annulus fibrosus (AF) that was allowed to contract for two weeks prior to loading. The discs were mechanically stimulated at a range of strain amplitude (1-10%) for two weeks with a duty cycle of 1hr on-1hr off-1hr on before being evaluated for their biochemical and mechanical properties. Mechanical loading increased all properties in a dose-dependent manner. GAGs increased between 2.8 and 2.2 fold in the AF and NP region respectively while hydroxyproline content increased between 1.2 and 1.8 fold. The discs also experienced a 2 fold increase in the equilibrium modulus, and a 4.3 fold increase in the instantaneous modulus. Full effects for all properties were seen by 5% strain amplitude. These data suggest that dynamic loading increases the functionality of our TE-IVDs with region-dependent responses using a method that may be scaled up to larger disc models expedite maturation for implantation.
    Tissue Engineering Part A 10/2014; 21(3-4). DOI:10.1089/ten.TEA.2014.0174 · 4.70 Impact Factor
  • [Show abstract] [Hide abstract]
    ABSTRACT: A herniated intervertebral disc often causes back pain when disc tissue is displaced through a damaged annulus fibrosus. Currently the only methods available for annulus fibrosus repair involve mechanical closure of defect, which does little to address biological healing in the damaged tissue. Collagen hydrogels are injectable and have been used to repair annulus defects in vivo. In this study, high-density collagen hydrogels at 5, 10 and 15 mg/ml were used to repair defects made to intact rat caudal intervertebral discs in vitro. A group of gels at 15 mg/ml were also crosslinked with riboflavin at 0.03 mM, 0.07 mM or 0.10 mM. These crosslinked, high-density collagen gels maintained presence in the defect under loading and contributed positively to the mechanical response of damaged discs. Discs exhibited increases to 95% of undamaged effective equilibrium and instantaneous moduli as well as up to four fold decreases in effective hydraulic permeability from the damaged discs. These data suggest that high density collagen gels may be effective at restoring mechanical function of injured discs as well as potential vehicles for delivery of biological agents such as cells or growth factors that may aid in the repair of the annulus fibrosus. This article is protected by copyright. All rights reserved.
    Journal of Biomedical Materials Research Part A 12/2014; DOI:10.1002/jbm.a.35388 · 2.83 Impact Factor
  • Source
    [Show abstract] [Hide abstract]
    ABSTRACT: Aim: To develop a biomimetic polymeric injectable hydrogel that can support nucleus pulposus (NP) regeneration. Materials & methods: Natural polymer-based hydrogels were synthesized using fibrinogen (FBG) and hyaluronic acid (HA), conjugated by a novel two-step procedure. Bovine NP cells were cultured in FBG-HA conjugate-based 3D beads in vitro and in a nucleotomized organ culture model. Results: FBG-HA conjugate-based hydrogels prepared with 235 KDa HA at a FBG/HA w/w ratio of 17:1 showed superior gel stability and mechanical properties and markedly increased glycosaminoglycan synthesis compared with a FBG/HA mixture-based hydrogels or fibrin gels. Gene-expression levels of NP markers were maintained in vitro. In organ culture, NP cells seeded in FBG-HA conjugate-based hydrogels showed better integration with native NP tissue compared with fibrin gels. Moreover, FBG-HA conjugate-based hydrogels restored compressive stiffness and disc height after nucleotomy under dynamic load. Conclusion: Specific FBG-HA conjugate-based hydrogels may be suitable as injectable materials for minimally invasive, biological NP regeneration.
    Regenerative Medicine 05/2014; 9(3):309-26. DOI:10.2217/rme.14.5 · 3.50 Impact Factor