Electronic and magnetic properties of MnSnAS(2)

Department of Physics and Astronomy, Northwestern University, Evanston, Illinois, United States
physica status solidi (b) (Impact Factor: 1.49). 06/2004; 241(7):1462 - 1465. DOI: 10.1002/pssb.200304641


We have synthesized MnSnAs2 single crystals using the vertical temperature gradient solidification method. The crystal structure of MnSnAs2 is chalcopyrites, which are “genealogically” related to the more familiar tetrahedrally-coordinated zinc-blende materials, with lattice constants of a = 5.794 Å, c = 11.365 Å. Using the experimentally determined lattice constants and crystal structure, we carried out first principles electronic structure calculations, using the full-potential linearized augmented plane wave (FLAPW) method in the local density approximation (LDA). The lowest total energies were observed for the AFM state, indicating that AFM ordering in the system is energetically favored at 0 K. We find that MnSnAs2 is metallic in the electronic calculation. Interestingly, MnSnAs2 exhibited ferromagnetism with TC = 328 K. (© 2004 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim)

Download full-text


Available from: Soon Cheol Hong,
  • Source
    • "Some of these compounds demonstrate magnetic properties when they are doped by magnetic impurities. Recent studies have shown that doping of A II B IV C V 2 chalcopyrite ternaries by high doses of Mn leads to an appearance of ferromagnetism [2] [3] [4] [5] [6] [7]. Such materials have lattice parameters close to substrates of interest such as Si, Ge and GaAs. "
    [Show abstract] [Hide abstract]
    ABSTRACT: Magnetic impurities in ternary semiconductors could spectacularly change its properties. To better understand the Mn effects, we have performed theoretical calculations of the atomic structure and electronic properties of Mn-doped ZnGeP2 chalcopyrite. The influence of the concentration and location of impurity atoms on magnetic properties is analysed. The possibilities of spintronic applications of the material are discussed.
    Microelectronics Reliability 09/2006; 46(9-11-9):1747-1749. DOI:10.1016/j.microrel.2006.08.006 · 1.43 Impact Factor
  • [Show abstract] [Hide abstract]
    ABSTRACT: We report the molecular beam epitaxy (MBE) growth of lightly Mn-doped Zn–Sn–As-based compounds on (001) InP substrates. Our XRD measurements showed peaks assignable to sphalerite-type ZnSnAs2:Mn, a supposition further supported by our EPMA and TEM analyses. The optimum substrate temperature TS resulting into the most stoichiometric ZnSnAs2 epitaxial films was first determined by growing undoped ZnSnAs2 at different TS of 265, 280, 300, and 320°C. The sample grown at TS=300°C showed the best stoichiometry according to our EPMA composition studies. We then prepared lightly Mn-doped ZnSnAs2 at this optimum substrate temperature of 300°C. Room temperature SQUID measurements revealed paramagnetic response with weak ferromagnetism as evident from the slightly S-shape M–H curve superimposed on a linearly increasing magnetization with increasing field.
    Journal of Crystal Growth 04/2007; 301:656-661. DOI:10.1016/j.jcrysgro.2006.12.015 · 1.70 Impact Factor
  • Source
    [Show abstract] [Hide abstract]
    ABSTRACT: Electronic and magnetic properties of BeSiAs2 and BeGeAs2 ternary compounds with chalcopyrite structure doped with transition metals (Mn, Cr) have been theoretically studied from the first principles. The influence of the substitutional positions of impurity atoms and their type on the appearance of a ferromagnetic (FM) or antiferromagnetic (AFM) state has been analyzed. It was found that magnetic moment of the systems does not depend strongly on the concentration and distance between impurity atoms, while the most important factors observed are the impurity type and substitution sites. Configurations with Mn atoms in the II-group sites are energetically stable in the AFM state, whereas Cr-doped ones seem to be in the FM state. Substitution of IV-group positions by both metals results preferably in the FM state, however these positions are not energetically favorable in comparison with II-group ones. The spin polarization of doped materials is evaluated and their possible application in spintronics is analyzed.
    Proceedings of SPIE - The International Society for Optical Engineering 01/2009; 7377. DOI:10.1117/12.836166 · 0.20 Impact Factor
Show more