Ethanol production by Kluyveromyces lactis immobilized cells in copolymer carriers produced by radiation polymerization.
ABSTRACT The conditions for batch and continuous production of ethanol, using immobilized growing yeast cells of Kluyveromyces lactis, have been optimized. Yeast cells have been immobilized in hydrogel copolymer carriers composed of polyvinyl alcohol (PVA) with various hydrophilic monomers, using radiation copolymerization technique. Yeast cells were immobilized through adhesion and multiplication of yeast cells themselves. The ethanol production of immobilized growing yeast cells with these hydrogel carriers was related to the monomer composition of the copolymers and the optimum monomer composition was hydroxyethyl methacrylate (HEMA). In this case by using batch fermentation, the superior ethanol production was 32.9 g L(-1) which was about 4 times higher than that of cells in free system. The relation between the activity of immobilized yeast cells and the water content of the copolymer carriers was also discussed. Immobilized growing yeast cells in PVA: HEMA (7%: 10%, w/w) hydrogel copolymer carrier, were used in a packed-bed column reactor for the continuous production of ethanol from lactose at different levels of concentrations (50, 100 and 150) g L(-1). For all lactose feed concentrations, an increase in dilution rates from 0.1 h(-1) to 0.3 h(-1) lowered ethanol concentration in fermented broth, but the volumetric ethanol productivity and volumetric lactose uptake rate were improved. The fermentation efficiency was lowered with the increase in dilution rate and also at higher lactose concentration in feed medium and a maximum of 70.2% was obtained at the lowest lactose concentration 50 g L(-1).
Article: Production of Prednisolone by Pseudomonas oleovorans Cells Incorporated Into PVP/PEO Radiation Crosslinked Hydrogels.[show abstract] [hide abstract]
ABSTRACT: In order to rise the yield of prednisolone from hydrocortisone, the Pseudomonas oleovorans cells were entrapped into radiation crosslinked poly (vinyl pyrrolidone)/poly(ethylene oxide) (PVP/PEO) hydrogel of different gel contents. The factors affecting the gel content and swelling behavior of the polymeric gel, such as polymer composition, polymer blend concentration, and irradiation doses, were investigated. The formation of gels having a good strength with the ability to retain a desirable amount of water in their three-dimensional network can be achieved by using PVP/PEO copolymer of composition $(90:10)$ and concentration of 15% prepared at 20 kGy irradiation dose. At these conditions the prepared hydrogel is considered the most favorable one that gave the highest hydrocortisone bioconversion and prednisolone yield, 81% and 62.8%, respectively. The improvement of prednisolone yield was also achieved by increasing substrate concentration. Maximum hydrocortisone bioconversion (86.44) was obtained at 18 hours by using substrate concentration of 30 mg. Reusability of immobilized Pseudomonas oleovorans entrapped into PVP/PEO copolymer hydrogel was studied. The results indicated that the transformation capacity of hydrocortisone to prednisolone highly increased by the repeated use of copolymer for 4 times. This was accompanied by an increase in prednisolone yield to 89% and the bioconversion of hydrocortisone was 98.8%.Journal of Biomedicine and Biotechnology 02/2004; 2004(4):219-226. · 2.44 Impact Factor